Patterns forming method

ABSTRACT

A patterns forming method begins with performing a lithography process on a photoresist film with a photomask having first apertures in a first mask region and second apertures in a second mask region to respectively form first main features and dummy features, on which the second mask region is located between the border of the photomask and the first mask region, and a size of each of the first apertures is greater than a size of each of the second apertures. Subsequently, a material is filled into the first main features to respectively form second main features and into the dummy features to seal the dummy features. Then, a substrate is etched to form patterned features by using the photoresist film having the second main features.

BACKGROUND Field of Invention

The present disclosure relates to a patterns forming method. More particularly, the present disclosure relates to forming uniformly patterned features on a semiconductor workpiece.

Description of Related Art

Conventional patterns forming method produces patterned features with scattering minimum feature sizes (CD) on a semiconductor workpiece, especially on the marginal area of a semiconductor workpiece. The uniformity of the minimum feature sizes of the patterned features may influence the electrical properties of the semiconductor workpiece, such as resistance, or impedance and so on. For example, a semiconductor workpiece on which patterned features with scattering minimum feature sizes are formed may hardly execute an impedance matching process to eliminate the white noise or other noise. That is, the scattering minimum feature sizes of the patterned features may induce the adjustment of a impedance matching process being ineffective.

As aforementioned, the patterns forming method on a semiconductor workpiece apparently exists problems of inconvenience and defects, and needs further improvement. To address the problems, the ordinarily skilled artisans have been striving to attain a solution, but still not to develop a suitable solution. Therefore, it is important to effectively deal with the problems in the art.

SUMMARY

The present disclosure provides a patterns forming method. The patterns forming method begins with performing a lithography process on a photoresist film with a photomask having first apertures in a first mask region and second apertures in a second mask region to respectively form first main features and dummy features, on which the second mask region is located between the border of the photomask and the first mask region, and a size of each of the first apertures is greater than a size of each of the second apertures. Subsequently, a material is filled into the first main features to respectively form second main features and into the dummy features to seal the dummy features. Then, a substrate is etched to form patterned features by using the photoresist film having the second main features.

According to an embodiment of the present disclosure, the filling of the material includes forming the material to fill the first main features and the dummy features of the photoresist film, and removing the material to form the second main features within the first main features.

According to an embodiment of the present disclosure, the removing of the material includes partially removing the material to make a through hole within each of the first main features while the dummy features is still sealed by the material, wherein the second main features are defined by the through holes.

According to an embodiment of the present disclosure, the performing of the lithography process on a photoresist film with the photomask includes exposing the photoresist film through the photomask, and forming the first main features and the dummy features by removing areas of the photoresist film exposed under the first apertures and the second apertures respectively.

According to an embodiment of the present disclosure, the exposing of the photoresist film through the photomask includes providing an exposure light having a central region, in which one or more row of the second apertures is located between the border of the central region and the first apertures.

According to an embodiment of the present disclosure, the patterns forming method further includes forming a hard mask between the substrate and the photoresist film.

According to an embodiment of the present disclosure, the etching of the substrate further includes etching the hard mask through the second main features to form third main features, and etching the substrate through the third main features.

According to an embodiment of the present disclosure, the first mask region is surrounded by the second mask region.

According to an embodiment of the present disclosure, the first apertures and the second apertures have similar geometry.

According to an embodiment of the present disclosure, the patterns forming method further includes forming the first apertures and the second apertures in a single process.

It is to be understood that both the foregoing general description and the following detailed description are by examples, and are intended to provide further explanation of the invention as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

The disclosure can be more fully understood by reading the following detailed description of the embodiment, with reference made to the accompanying drawings as follows:

FIG. 1 is a flow chart of a patterns forming method according to some embodiments of the present disclosure.

FIG. 2A is a schematically top view of a photomask according to some embodiments of the present disclosure.

FIG. 2B is a cross-sectional view of a semiconductor workpiece and a photomask at a stage of a patterns forming method according to some embodiments of the present disclosure.

FIG. 3A is a schematically top view of a semiconductor workpiece according to some embodiments of the present disclosure.

FIG. 3B is a cross-sectional view of a semiconductor workpiece at a stage of a patterns forming method according to some embodiments of the present disclosure.

FIG. 4 is a cross-sectional view of a semiconductor workpiece at a stage of a patterns forming method according to some embodiments of the present disclosure.

FIG. 5A is a schematically top view of a semiconductor workpiece according to some embodiments of the present disclosure.

FIG. 5B is a cross-sectional view of a semiconductor workpiece at a stage of a patterns forming method according to some embodiments of the present disclosure.

FIG. 6A is a schematically top view of a semiconductor workpiece according to some embodiments of the present disclosure.

FIG. 6B is a cross-sectional view of a semiconductor workpiece at a stage of a patterns forming method according to some embodiments of the present disclosure.

FIG. 7 is a cross-sectional view of a semiconductor workpiece at a stage of a patterns forming method according to some embodiments of the present disclosure.

Corresponding numerals and symbols in the different figures generally refer to corresponding parts unless otherwise indicated. The figures are drawn to dearly illustrate the relevant aspects of the embodiments and are not necessarily drawn to scale.

DETAILED DESCRIPTION

Reference will now be made in detail to the present embodiments of the invention, examples of which are illustrated in the accompanying drawings. Wherever possible, the same reference numbers are used in the drawings and the description to refer to the same or like parts.

It will be understood that when an element is referred to as being “on” another element, it can be directly on the other element or intervening elements may be present therebetween. In contrast, when an element is referred to as being “directly on” another element, there are no intervening elements present.

Reference is made to FIG. 1. FIG. 1 illustrates a flow chart of a patterns forming method 100 according to some embodiments. As shown in FIG. 1, the patterns forming method 100 begins with step S110 in which a lithography process is performed on a photoresist film with a photomask having first apertures in a first mask region and second apertures in a second mask region to respectively form first main features and dummy features. The second mask region is located between the border of the photomask and the first mask region. Namely, the second apertures are formed between the border of the photomask and the first apertures. In some embodiments, a size of each of the first apertures is greater than a size of each of the second apertures, which can generate first main features with a greater size compared to the dummy features on the photomask. Subsequently, the patterns forming method 100 continues with step 120 in which a material is filled into the first main features to form second main features, and filling the material into the dummy features to seal the dummy features. Then, the patterns forming method 100 continues with step 130 in which a substrate is etched by using the photoresist film having the second main features.

Owing to the second apertures can assist the first aperture to form the first main features uniformly under the lithography process; and moreover, the dummy features, formed by the second apertures, can be sealed to avoid further being transferred, the patterns forming method 100 are enable to form the second main features, with a better uniformity, within the first main features. The second main features can be used for subsequently processes, such as etching process, to transfer the second main features onto the underlying layers of a semiconductor workpiece. For example, the underlying layers may include a substrate or a hard mask layer. Owing to the uniformity of the second main features, the second main features can also generate patterned features with uniform minimum feature size (CD) in the underlying layers. That is to say, the patterns forming method 100 employs the photomask with the second apertures between the first apertures and the border of the photomask, to produce a semiconductor workpiece on which with patterned features with uniform minimum feature size are formed. While avoiding or preventing the photoresist and underlying layers formed features with scattering sizes, especially to regions proximal to the border of the photoresist and underlying layers, the semiconductor workpiece formed by the patterns forming method 100 may acquire better electrical properties. For example, the semiconductor workpiece can execute impedance matching process more easily to eliminate the noise.

In addition, owing to the marginal effect of the lithography process may further enhance the difference of sizes between the uniform first main features and the dummy features, the dummy features can be filled or eliminated more easily. As a consequence, a size of the second main features can be adjusted to actual demand by varying the difference of sizes between the first main features and the dummy features. On the other hand, adjusting a ratio between the size of the first apertures and the size of the second apertures could vary the size of the second main features to fulfill actual demand.

Reference is made to FIG. 2A and FIG. 2B. FIG. 2A illustrates a schematically top view of a photomask 200 according to some embodiments. FIG. 2B illustrates a cross-sectional view of a semiconductor workpiece 300 and a photomask 200 at a stage of a patterns forming method 100 according to some embodiments. As shown in FIG. 2A, in some embodiments, the photomask 200 has a first mask region 220 on which first apertures 222 are formed, and a second mask region 240 on which second apertures 242 are formed. The second mask region 240 is located between the border of the photomask 200 and the first mask region 220. In some embodiments, the first mask region 220 can be surrounded by the second mask region 240, such that the first main features 322 (as shown in FIG. 3A, 3B) correspondingly formed by the first mask region 220 can be formed uniformly in every directions.

In some embodiments, the first apertures 222 and the second apertures 242 of the photomask 200 may have similar geometry. The first apertures 222 and the second apertures 242 can be square, rectangle, circle, ellipse, or other suitable shape. In some embodiments, the first apertures 222 and the second apertures 242 can be formed in a single process, to save processing time and photomasks used to fabricate the photomask 200. In other embodiments, the first apertures 222 and the second apertures 242 can be formed separately.

It should be noted that, the geometry properties of the first apertures 222 and the second apertures 242, described herein, such as shape, or density . . . etc., is only exemplary, not intended to limit the present disclosure. For example, if the geometry of the first apertures 222 and the second aperture 242 are circle, the size of the first apertures 222 and the second aperture 242 can be measured by diameters. For another example, if the geometry of the first apertures 222 and the second aperture 242 are square, the size of the first apertures 222 and the second aperture 242 can be measured by radius, area, or perimeter . . . etc. On the other hand, the size of the first apertures 222 and the second aperture 242 can be measured by sectional area. It should be understood that, the geometry properties of the first apertures 222 and the second apertures 242 could be adjusted to actual demand by those skilled in the art, without departed from the scope or the spirits of the present disclosure. The prerequisite of the first apertures 222 and the second apertures 242 is that the second apertures 242 has a smaller size compared to the first apertures 222, and can assist the first apertures 222 to form the first main features 322 uniformly on a photoresist film 320 (as shown in FIG. 3A).

Referring to the FIG. 2B, the photomask 200, shown in FIG. 2B, can be regard as a cross-sectional view of the photomask 200 taken along line A-A′ in FIG. 2A. In some embodiments, the photomask 200 is adopted to perform a lithography process on a photoresist film 320 of the semiconductor workpiece 300. In some embodiment, the performing of the lithography process may include exposing the photoresist film 320 through the photomask 200. An exposure light 400 may be provided to perform the exposing of the photoresist film 320. In some embodiments, the exposure light 400 has a light field substantially divided into a central region 420 and a marginal region 440. In some embodiments, one or more row of the second apertures 342 is located between the border of the central region 420 and the first apertures 322. Therefore, the second apertures 342 can function to assist the first apertures 322 forming the first main features 322. In some embodiments, the first main features 322 are defined as the areas of the photoresist film exposed through the first apertures (as shown in FIG. 3B) under the central region 420 of the exposure light 400. In other embodiments, a light field of an exposure light 400 may be flat field or other suitable shape of the light field. Regardless of the shape of the light field, one or more row of the second apertures 342 need to be located between the border of the exposure light 400 and the first apertures 322.

Reference is made to FIG. 3A and FIG. 3B. FIG. 3A illustrates a schematically top view of a semiconductor workpiece 300 according to some embodiments. FIG. 3B illustrates a cross-sectional view of a semiconductor workpiece 300 and a photomask 200 at a stage of a patterns forming method 100 according to some embodiments of the present disclosure, in which the photoresist film 320, shown in FIG. 3B, can be regard as a cross-sectional view of the photoresist film 320 taken along line B-B′ in FIG. 3A. Referring to the FIG. 3A and FIG. 3B, the first main features 322 and the dummy features 324 are formed on the photoresist film 320. In some embodiments, areas of the photoresist film 320 exposed under the first apertures 222 and the second apertures 242 are removed by developer, to form the first main features 322 and the dummy features 324 respectively.

Owing to the second apertures 242 assisted the first apertures 222 forming the first main features 322, as shown in FIG. 3A and FIG. 3B, the geometry properties of the first main features 322 are substantially the same. Therefore, the first main features 322 of the photoresist film 320 can have a better uniformity while applying the photomask 200 with the first apertures 222 and the second apertures 242 to perform lithography processes on the photoresist film 320, to avoid or prevent the size of each of the first main features 322 on the photoresist film 320 from being scattering, which may form the uniform second main features subsequently.

Reference is made to FIG. 4. FIG. 4 illustrates a cross-sectional view of a semiconductor workpiece 300 at a stage of a patterns forming method 100 according to some embodiments of the present disclosure. As shown in FIG. 4, in some embodiments, a material 330 is formed to substantially fill up the first main features 322 and the dummy features 324 of the photoresist film 320. In other embodiments, the material 330 can be formed to substantially fully cover or block the first main features 322 and the dummy features 324. In some embodiments, the material 330 can be a water-based material, or an organic-based material. In some embodiment, the material 330 can be a resolution enhancement lithography assisted by chemical shrink (RELACS) material, a thermal material, or other suitable materials.

Reference is made to FIG. 5A and FIG. 5B. FIG. 5A and FIG. 5B respectively illustrate a schematically top view and a cross-sectional view of a semiconductor workpiece 300 at a stage of a patterns forming method 100 according to some embodiments, in which FIG. 5B can be regard as a cross-sectional view of the material 330 taken along line C-C′ in FIG. 5A. As show in FIG. 5A and FIG. 5B, the material 330 are removed from the first main features 322, and formed the second main features 350 within the first main features 322. In some embodiments, the material 330 are partially removed from the first main features 322, to make a through hole within each of the first main features 322, while the dummy features 324 is still sealed by the material. The second main features 350 are defined by the through holes. Therefore, the second main features 350 of the photoresist film 320 may be uniform in geometry, so that the photoresist film 320 having the second main features 350 can be used to etching a substrate 360 underneath, for transferring the second main features 350 to form patterned features with a better uniformity on the substrate 360.

It should be noted that, the filling of the material 330, described herein, is only an exemplary, and not intended to limit the present disclosure. In other embodiments, the material 330 formed inside the dummy features 324 may be partially removed while the end of the dummy features 324 remaining sealed. In other embodiments, the material 330 may be formed to shrink the size of the first main features 322 and the dummy features 324 till the dummy features 324 being eliminated or blocked by the material 330. It should be understood that, the filling of the material 330 could be adjusted to actual demand by those skilled in the art, without departed from the scope or the spirits of the present disclosure. The prerequisite of the filling of the material 330 is that the dummy features 324 are eliminated or blocked to form blind holes, and stopped for further transferred.

Referring back to the FIG. 5B, in some embodiments, the semiconductor workpiece 300 may further include a hard mask 340 formed between the substrate 360 and the photoresist film 320. Subsequently, the second main features 350 can be transferred onto the hard mask 340 before etching the substrate 360.

Reference is made to FIG. 6A, FIG. 6B and FIG. 7. FIG. 6A and FIG. 6B respectively illustrates a schematically top view and a cross-sectional view of a semiconductor workpiece 300 at a stage of a patterns forming method 100 according to some embodiments, in which FIG. 6B can be regard as a cross-sectional view of the hard mask 340 taken along line D-D′ in FIG. 6A. As shown in FIG. 6A and FIG. 6B, the hard mask 340 is etched to form third main features 342 through the second main features 350 of the photoresist film 320 (as shown in FIG. 5B). Subsequently, the photoresist film 320 are removed, to expose the hard mask 340. Owing to the unifomity of the second main features 350, consequently, the third main features 342 correspondingly formed by the second main features 350 may also inherited the unifomity.

FIG. 7 illustrates a cross-sectional view of a semiconductor workpiece 300 at a stage of a patterns forming method 100 according to some embodiments. Referring to FIG. 6B and FIG. 7, in some embodiment, subsequently, the substrate 360 can be etched through the third main features 342, to form features 362 on the substrate 360, and then the hard mask 340 can be removed to produce a semiconductor workpiece 300 with uniform features 362 formed inside the substrate 360. Therefore, the semiconductor workpiece 300 may have better electrical properties.

Summarized from the above description, the present disclosure provides a patterns forming method including performing a lithography process on a photoresist film with a photomask having first apertures in a first mask region and second apertures in a second mask region to respectively form first main features and dummy features, in which the second mask region is located between the border of the photomask and the first mask region, and a size of each of the first apertures is greater than a size of each of the second apertures; filling a material into the first main features to respectively form second main features, and into the dummy features to seal the dummy features; and etching a substrate by using the photoresist film having the second main features to form patterned features.

Although some embodiments of the present disclosure and their advantages have been described in detail, it should be understood that various changes, substitutions, and alterations can be made herein without departing from the spirit and scope of the disclosure as defined by the appended claims. For example, it will be readily understood by those skilled in the art that many of the features, functions, processes, and materials described herein may be varied while remaining within the scope of the present disclosure. Moreover, the scope of the present application is not intended to be limited to the particular embodiments of the process, machine, fabricate, composition of matter, means, methods, and steps described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure of the present disclosure, processes, machines, fabricate, compositions of matter, means, methods, or steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the present disclosure. Accordingly, the appended claims are intended to include within their scope such processes, machines, fabricate, compositions of matter, means, methods, or steps. 

What is claimed is:
 1. A patterns forming method comprising: performing a lithography process on a photoresist film with a photomask having a plurality of first apertures in a first mask region and a plurality of second apertures in a second mask region to respectively form a plurality of first main features and a plurality of dummy features, wherein the second mask region is located between the border of the photomask and the first mask region, and a size of each of the first apertures is greater than a size of each of the second apertures; filling a material into the first main features to respectively form a plurality of second main features and into the dummy features to seal the dummy features; and etching a substrate by using the photoresist film having the second main features.
 2. The patterns forming method of claim 1, wherein the filling of the material comprises. forming the material to fill the first main features and the dummy features of the photoresist film; and removing the material to form the second main features within the first main features.
 3. The patterns forming method of claim 2, wherein the removing of the material comprises partially removing the material to make a through hole within each of the first main features while the dummy features is still sealed by the material, wherein the second main features are defined by the through holes.
 4. The patterns forming method of claim 1, wherein the performing of the lithography process on a photoresist film with the photomask comprises: exposing the photoresist film through the photomask; and forming the first main features and the dummy features by removing areas of the photoresist film exposed under the first apertures and the second apertures respectively.
 5. The patterns forming method of claim 4, wherein the exposing of the photoresist film through the photomask comprises providing an exposure light having a central region, wherein one or more rows of the second apertures are located between the border of the central region and the first apertures.
 6. The patterns forming method of claim 1, further comprising forming a hard mask between the substrate and the photoresist film.
 7. The patterns forming method of claim 6, wherein the etching of the substrate further comprising: etching the hard mask through the second main features to form a plurality of third main features; and etching the substrate through the third main features.
 8. The patterns forming method of claim 1, wherein the first mask region is surrounded by the second mask region.
 9. The patterns forming method of claim 1, wherein the first apertures and the second apertures have similar geometry.
 10. The patterns forming method of claim 1, further comprising forming the first apertures and the second apertures in a single process. 